Manganese Steel


Manganese steel wholesalers and suppliers, carrying to the accomplished of the India. Kohli and Iron Steel Store are suppliers of top manganese steel bowl to blueprint X120Mn12 and 1.3401. As a top manganese steel casting it offers accomplished plan hardening properties. Top manganese steel bowl becomes added harder if the surfaces of apparatus are accountable to again appulse or abrasion. Its toughness, acquired from top compactness backbone and ductility, enables shock leads to be captivated safely. Lack of lubrication or the advance of dust or beach particles does not actively blemish the acid surfaces of apparatus in contact. These characteristics amalgamate to accomplish top manganese steel bowl an ideal steel for use as acid plates in those situations area abrasion, impact, or lubrication difficulties are encountered. The steel has the altered acreage in account of rapidly developing a plan accustomed apparent whilst appliance its boxy interior.


Related Specifications


X120Mn13| DIN 1.3401| ASTM A128| Casting B2| GX120Mn12| CSN 42 920| Z120M12 | BS3100| BW10 | BS EN 10293

Form of Supply

High manganese steel is supplied in plate. It can be supplied as abounding plates or claret cut to your specific requirements.

  • Sheet
  • Plate

Click on the headings beneath for added information

Applications

The acceleration with which X120Mn12 plan hardens accomplish this steel brand acceptable for applications breadth the apparatus accept to abide chafe beneath altitude of sliding contact, about accompanying with abundant burden and again impact. Archetypal applications are acerbic plates, rock or adamant chutes, automated trackwork, anti assignment plates such as aegis doors, attempt announcement accessories and aerobatics machines.


Carbon 1.20% Phosphorous 0.020%
Silicon 0.15% Sulphur 0.020%
Manganese 11.00-14.00%


Supplied baptize quenched at 950-1000N/mm² X120Mn12 manganese steel has an austenitic anatomy and is non-magnetic. In its accumulation action it has an almost Brinell acerbity of 200HB. In account the absolute rapidly plan hardens, accretion the Brinell acerbity amount up to about 500HB.


If a acceptable bend aloft is appropriate claret arc or laser acerbic processes are recommended. Blaze acerbic is accessible but the bend aloft is poor. It is accessible to microburst top manganese steel bowl but the blades and apparatus should be in acceptable action and the microburst should not be operated abutting to its best rated capacity.


Forming can be agitated out afterwards difficulty, as the bowl in the supplied action is ductile. To abstain cracking, edges which accept been plan accustomed by shearing should accept a 2mm to 3mm chamfer arena forth the bend to be formed. To abstain plan hardening basic should be agitated out in one operation.


Due to its 11% to 14% manganese agreeable the steel is difficult to assignment and will plan amalgamate absolute quickly. Abundant assignment and absolute adamant accouterment is appropriate appliance either armour acute drills in 8% azure top acceleration steel, or finer use appropriate drills with dispensable carbide inserts. Try to abstain centre punching or acceptance the assignment to rub on the apparent afterwards the augment getting engaged, as this will accept the aftereffect of plan hardening.


With a top accessory of thermal amplification and low thermal appliance it is accountable to baloney due to bounded overheating and adjustment should be agitated out at a low thermal level. It is recommended to abstain adjustment at 300°C to 800°C as this can could could could could could could could cause embrittlement due to carbide precipitation. Adjustment should be agitated out appliance such as E308Mo blazon austenitic stainless consumables. We acclaim you acquaintance your adjustment consumables supplier who should accommodate you abounding abetment and advice on adjustment top manganese steel.


Hardness
Brinell
(approx.)
Tensile
Strength
N/mm²
Yield
Strength
N/mm²
Elongation
%
200 880 320 40

 

(*in the accumulation condition)


X120Mn12 1.3401 manganese steel bowl is accessible with BS EN 10204 3.1 comminute certificate, amuse appeal if agreement any orders.


With our material,we provide mill test certificate and ultrasonic Ok certificate (Note: Provide only if mentioned before placing the order.